Range

 Coexistence Equation

 Standard Free Energy Change

(K)

 (Oxidation Reaction)

 (J)

900-1154

 Pd + 0.5 O2 = PdO

 -114,200 + 100 T (°K)

884-1126

 2 Mn304 + 0.5 O2 = 3 Mn2O3

 -113,360 + 92.0 T

298-1300

 3 CoO + 0.5 O2 = Co3O4

 -183,200 + 148 T

892-1302

 Cu2O + 0.5 O2 = 2 CuO

 -130,930 + 94.5 T

1396-1723

 1.5 UO2 + 0.5 O2 = 0.5 U3O8

 -166,900 + 84 T

878-1393

 U4O9 + 0.5 O2 = 4/3 U3O8(-2)

 -164,400 + 82 T

967-1373

 2 Fe3O4 + 0.5 O2 = 3 Fe2O3

 -246,800 + 141.8 T

1489-1593

 2 Cu + 0.5 O2 = Cu2O

 -166,900 + 43.5T

1356-1489

 2 Cu + 0.5 O2 = Cu2O

 -190,300 + 89.5 T

924-1328

 2 Cu + 0.5 O2 = Cu2O

 -166,900 + 71.1 T

992-1393

 3 MnO + 0.5 O2 = Mn3O4

 -222,540 + 111 T

1160-1371

 Pb + 0.5 O2 = PbO

 -190,580 + 74.9 T

772-1160

 Pb + 0.5 O2 = PbO

 -215,000 + 96.0 T

911-1376

 Ni + 0.5 O2 = NiO

 -233,580 + 84.9 T

1173-1373

 Co + 0.5 O2 = CoO

 -235,900 + 71.5 T

973-1273

 10 WO2.90 + O2 = 10 WO3

 -279,400 + 112 T

973-1273

 10 WO2.72 + O2 = 10 WO2.90

 -284,000 + 101 T

973-1273

 1.39 WO2+0.5 O2 = 1.30 W O2.72

 -249,310 + 62.7 T

973-1273

 0.5 W + 0.5 O2 = 0.5 WO2

 -287,400 + 84.9 T

949-1273

 3 FeO + 0.5 O2 = Fe3O4

 -311,600 + 123 T

770-980

 Sn + 0.5 O2 = SnO2

 -293,230 + 108 T

903-1540

 Fe + 0.5 O2 = FeO

 -263,300 + 64.8 T

1025-1325

 0.5 Mo + 0.5 O2 = 0.5 MoO2

 -287,600 + 83.7 T

1050-1300

 2 NbO2 + 0.5 O2 = Nb2O5

 -313,520 + 78.2 T

693-1181

 Zn + 0.5 O2 = ZnO

 -355,890 + 107.5 T

1300-1600

 0.66 Cr + 0.5 O2 = 0.33 Cr2O3

 -371,870 + 83.7 T

1050-1300

 NbO + 0.5 O2 = NbO2

 -360,160 + 72.4 T

923-1273

 Mn + 0.5 O2 = MnO

 -388,770 + 76.3 T

1539-1823

 Mn + 0.5 O2 = MnO

 -409,500 + 89.5 T

1073-1273

 0.4 Ta + 0.5 O2 = 0.2 Ta2O5

 -402,400 + 82.4 T

1050-1300

 Nb + 0.5 O2 = NbO

 -420,000 + 89.5 T

298-1400

 0.5 U + 0.5 O2 = 0.5 UO2

 -539,600 + 83.7 T

1380-2500

 Mg(v) + 0.5 O2 = MgO

 -759,600 - 30.83 T log T + 317 T

923-1380

 Mg(l) + 0.5 O2 = MgO

 -608,200 - 1.00 T log T + 105 T

1124-1760

 Ca + 0.5 O2 = CaO

 -642,500 + 107 T

1760-2500

 Ca(v) + 0.5 O2 = CaO

 -795,200 + 195 T